ANSERGLOB BCX 33

The surface preparation is realized according to State Standard of Ukraine (DSTU N B A.3.1-23:2013, DSTU N B A.2.6-212:2016) and State Building Codes of Ukraine (DBN В.2.6-162:2010). Surface must be structurally sound, clean, dry and free from dust, grease, dirt, lime, wax, oil or emulsion paints. Fragile areas of substrate must be removed. Surface irregularity till 10 mm must be leveled by mortar ANSERGLOB BCX 33, big irregularities of walls – by the plastering mortar ANSERGLOB ВСТ 20 and big irregularities of floors of by cement screed ANSERGLOB LFS 69 or ANSERGLOB LFS 70. Before applying substrates with strong sorption must be treated by one of deeply penetrating emulsions ANSERGLOB and exposed for 4 hours. Before applying substrates with low sorption must be treated by ANSERGLOB EG 62 or ANSERGLOB EG 63 BETON KONTAKT and exposed from 3 to 6 hours.

Prepared mortar should be spread by tile trowel, spatula or float on cladding surface. After applied mortar is combed by notch trowel or spatula with the U-shaped notches or square notches, which form equal combs of the same altitude on applied surface. Depending on thickness and dimensions of cladding tiles notch size of trowel is selected (for example, for tile size 20x20 cm trowels with the square notch size 6 mm and more are used). Tiles are installed in turn on the surface, covered by adhesive mortar, and pressed evenly. The tile can be moved during 10 min from the moment of installation if required. Thickness of adhesive layer between tile and substrate must be minimally 2 mm to show its full curing. Using handmade tile with unleveled back side and some cut ceramic and stone tile additional spreading of adhesive mortar by rectangular trowel on tile back side is required in order to achieve full contact between tile and substrate. Applying of adhesive mortar on back side of tile is additional measure and does not replace its spreading on the substrate. Joint width between tiles must be not less than 1,5 mm.
Tiles are prohibited to wet preliminary!

NOTE

If the bag is marked WINTER, the mortar is used at a temperature more then 0 °C. During the period of gaining strength of the mortar, it is allowed to reduce the ambient temperature to -5 ° C. The base for the mortar should not be frozen. All the above recommendations are effective at a relative humidity of 60%. In other conditions, the time of peeling, setting and curing may change. When performing works, the facade must be protected from high humidity (rain, fog, snow).

The work should be performed at a temperature of + 5° C to + 300C. All the above recommendations are effective at a temperature of + 20° C and a relative humidity of 60%. In other conditions, the time of peeling, setting and curing may change. When performing works, the facade should be protected from direct sunlight, as well as high humidity (rain, fog).

Tile size, сm	Spatula tooth dimensions, mm	Average product consumption,kg/m2 (depends on the size of the tile and the  spatula)
less than 5 х 5	3	1,9
5х5 - 10х10	4	2,5
10х10 - 20х20	6	3,8
20х20 - 30х30	8	5
30х30 - 40х40	10	6,3
40х40	12	7,5

Dry mixture must be poured into container with clear water according to ratio 0,21 – 0,25 liters of water per 1 kg of mixture (5,25 –6,25 liters of water per 1 bag of 25 kg) when at the same time manually or mechanically mixed (by the drill on low revs) to obtain the kindred and elastic mass. After exposing 5 min mortar must be mixed again and used during 2 hours.