ANSERGLOB BCX 33 winter

Substrate preparation is carried out according to DSTU-N B A.3.1-23:2013 and DSTU-N B V.2.6-212:2016. The substrate must be strong, cleaned of dust, dirt, lime, oils, grease, wax, oil-based or emulsion paints. Remove unsound sections of the substrate. Surface irregularities up to 10 mm should be leveled with adhesive ANSERGLOB BCX 33. Larger wall irregularities should be leveled with ANSERGLOB BCT 20 plaster mortar, larger floors irregularities with ANSERGLOB LFS 69 or ANSERGLOB LFS 70 cement screed. Highly absorbent substrates must be treated with one of the ANSERGLOB deep penetration primers before work and allowed to dry for 4 hours. Low-absorbent substrates should be treated with ANSERGLOB EG 62 or ANSERGLOB EG 63 BETON KONTAKT primer and allowed to dry for 3–6 hours.

Prepared mortar should be spread by tile trowel, spatula or float on cladding surface. After applied mortar is combed by notch trowel or spatula with the U-shaped notches or square notches, which form equal combs of the same altitude on applied surface. Depending on thickness and dimensions of cladding tiles notch size of trowel is selected (for example, for tile size 20x20 cm trowels with the square notch size 6 mm and more are used). Tiles are installed in turn on the surface, covered by adhesive mortar, and pressed evenly. The tile can be moved during 10 min from the moment of installation if required. Thickness of adhesive layer between tile and substrate must be minimally 2 mm to show its full curing. Using handmade tile with unleveled back side and some cut ceramic and stone tile additional spreading of adhesive mortar by rectangular trowel on tile back side is required in order to achieve full contact between tile and substrate. Applying of adhesive mortar on back side of tile is additional measure and does not replace its spreading on the substrate. Joint width between tiles must be not less than 1,5 mm.
Tiles are prohibited to wet preliminary!

NOTE

If the bag is marked WINTER, the mortar of adhesive and reinforcing ANSERGLOB BCX 40 is used at a temperature more then 0 °C. During the period of gaining strength of the mortar, it is allowed to reduce the ambient temperature to -5 ° C. The base for the mortar should not be frozen. All the above recommendations are effective at a relative humidity of 60%. In other conditions, the time of peeling, setting and curing may change. When performing works, the facade must be protected from high humidity (rain, fog, snow).

The work should be performed at a temperature of + 50C to + 300C. All the above recommendations are effective at a temperature of + 200C and a relative humidity of 60%. In other conditions, the time of peeling, setting and curing may change. When performing works, the facade should be protected from direct sunlight, as well as high humidity (rain, fog).

Tile size, сm	Spatula tooth dimensions, mm	Average product consumption,kg/m2 (depends on the size of the tile and the  spatula)
less than 5 х 5	3	1,9
5х5 - 10х10	4	2,5
10х10 - 20х20	6	3,8
20х20 - 30х30	8	5
30х30 - 40х40	10	6,3
40х40	12	7,5

Dry mixture must be poured into container with clear water according to ratio 0,21-0,25 liters of water per 1 kg of mixture (5,25 –6,25 liters of water per 1 bag of 25 kg) when at the same time manually or mechanically mixed (by the drill on low revs) to obtain the kindred and elastic mass. After exposing 5 min mortar must be mixed again and used during 2 hours.